伊萨OK Autrod 4047 ER4047铝硅焊丝

OK Autrod 4047铝硅焊丝

品牌：瑞典伊萨

铝焊丝标准：GB/T10858-2008  AWS A5.10

焊丝直径：1.2、1.6、2.0、2.4、3.0、3.2、4.0、5.0(mm)

焊丝盘尺寸：D300（9kg）、D270（7kg）、D200（2kg）、D100（0.5kg）

包装状态：盘丝、直条

焊丝特点：12%硅含量，流动性好，焊接温度低。

推荐焊接方法：钎焊（俗称：氧气焊、火焰焊），配201铝焊粉。

焊接应用：焊接以下铝合金——汽车铝水箱、中冷器、散热器、铝合金客车窗、自行车车架、铝件维修。                                                                      

OK Autrod 4047

GMAW

OK Autrod 4047 was originally developed as a brazing alloy to take advantage of its low melting point and narrow freezing range. In addition, it has a higher silicon content than OK Autrod 4043, which provides increased fluidity and reduced shrinkage. The alloy produces bright, almost smut-free welds. Hot cracking is significantly reduced when using OK Autrod 4047 as a filler alloy. The alloy can be used in applications with sustained elevated temperatures. Non-heat treatable.

Welding current

DC( )

Classifications Approvals Typical all weld metal composition, %Typical mech. properties all weld metal

SFA/AWS A5.10 ER4047

EN ISO 18273

S Al 4047 (AlSi12)

CWB AWS A5.10 (Item number ending with A)

Si 12,0  Mn <0,15  Cu <0,05  Ti <0,15  Zn <0,20  Fe <0,6

Wire composition

Yield stress, MPa 80

Tensile strength, MPa 170

Elongation, %  12

Elongation, %  12

Diameter, mm         0,9     1,2     1,6

Arc voltage, V      13-24   20-29   25-30

Welding current, A  60-170 140-260 190-350

Wire feed, m/min      -      6-13  4,5-7,5

Deposition rate kg weld metal/hour - 1,1-2,4 1,5-2,5